Functionalized Bisphenol A-Based Polymer for High-Performance Structural Supercapacitor Composites.

Abstract

Over the last few decades, polymer composites have been rapidly making inroads in critical applications of electrical storage devices such as batteries and supercapacitors. Structural supercapacitor composites (SSCs) have emerged as multifunctional materials capable of storing energy while bearing mechanical loads, offering lightweight and compact solutions for energy systems. This study investigates the functionalization of Bisphenol A-based thermosetting polymers with ionic liquids, aiming to synthesize dual-functional structural electrolytes for SSC fabrication. A multifunctional sandwich structure was subsequently fabricated, in which the fabricated SSC served as the core layer, bonded between two structurally robust outer skins. The core layer was fabricated using carbon fibre layers coated with 10% graphene nanoplatelets (GNPs), while the skin layers contained 0.25% GNPs dispersed in the resin matrix. The developed device demonstrated stable operation up to 85 °C, achieving a specific capacitance of 57.28 mFcm^-2 and an energy density of 179 mWhm^-2 at room temperature. The performance doubled at 85 °C, maintaining excellent capacitance retentions across all experimented temperatures. The flexural strength of the developed sandwich SSC at elevated temperature (at 85 °C) was 71 MPa, which exceeds the minimum requirement for roofing sheets as specified in Australian building standard AS 4040.1 (Methods of testing sheet roof and wall cladding, Method 1: Resistance to concentrated loads). Finite element analysis (FEA) was performed using Abaqus CAE to evaluate structural integrity under mechanical loading and predict damage initiation zones under service conditions. The simulation was based on Hashin's failure criteria and demonstrated reasonable accuracy. This research highlights the potential of multifunctional polymer composite systems in renewable energy infrastructure, offering a robust and energy-efficient material solution aligned with circular economy and sustainability goals.